HYDRO-W10
TWO COMPONENT FLEX UV RESISTANT WATER ISOLATION PRODUCT / White Flex

White cement and polymer emulsion based, antibacterial, highly water repellent, modified with special additives, two component, UV resistant, flexible, water isolation material (20 kg powder + 10 kg liquid component)

TDS MSDS

TSE ISO CE


PRODUCT ADVANTAGES

  • HYDRO-W10 UV Resistant Flex Water Isolation Product provides labor & time advantage due to it’s easy preparation and application features.
  • Provides high adhesion, UV resistance and water isolation.
  • Provides less consumption at unit area by it’s special formula.
  • Provides an ideal economic waterproofing solution without joints under the coating materials by it’s flexible feature.
  • Antibacterial, prevents formation of mold-fungus-moss.
  • Resistant to freeze & thaw circle, chlorinated water and lime water, protects concrete surface against carbonation and chloride effects.
  • Proper for drinking water tank and pools, conformity certificate is available.

APPLICATION AREAS

Applied by a roller or brush to provide a high quality, smooth, non-shrink, flexible, UV resistant, water proofing surface before coating material applications on concrete surfaces which will be used as wet area (spa, bathroom, kitchen, balcony, terrace, pool, water tank, etc.) and also for water insulation of foundation walls, retaining walls, basements, water channels, etc. as horizontal and vertical at indoors and outdoors.

UNIT CONSUMPTION

18 m² / 20 kg + 10 kg set (Application Thickness: 1mm x 1 layers) 9 m² / 20 kg + 10 kg set (Application Thickness: 1mm x 2 layers)

TS EN 14891 / 04.2017 Applied As Liquid, Normal Cement Based Water Isolation Product, With Crack Covering Feature and Resistant To Chlorinated and Lime Water (Type: CM, Class: P)
Initial Adhesion Strength ≥ 0,5 N/mm²
Adhesion Strength After Heat Ageing ≥ 0,5 N/mm²
Adhesion Strength After Freeze And Thaw ≥ 0,5 N/mm²
Adhesion Strength After Contact With Water ≥ 0,5 N/mm²
Adhesion Strength After Contact With Lime Water ≥ 0,5 N/mm²
Adhesion Strength After Contact With Chlorinated Water ≥ 0,5 N/mm²
Water Impermeability ≤ 20 g mass increase
Crack Bridging Ability ≥ 0,75 mm (+20ºC)
Workability Time 30 min.
Time Required For Upper Application 3 days

PREPARING SURFACE

  • Application surface should be clean, sound and free from dust.
  • Adhesion barrier materials (oil, dirt, dust, etc.) should be cleaned, cement-mortar residues should be scraped.
  • Gaps and cracks on surface should be repaired with G-REPAIR-1200 or G-REPAIR-800 repair mortars at least 1 day before the application.
  • If needed, surface should be cleaned with water, excess water should be removed.
  • PRIMER-ST primer should be used at least 1 hour before the application to reduce water absorption of the surface and to provide better adhesion.

APPLICATION METHODS

20 kg HYDRO-W10 powder comp. is added on 10 kg HYDRO-UV10 liquid component by sprinkling.
Blended by a low speed mixer to that no lumps in it. Mortar is rested for 3 minutes to mature and mixed again before application.
Mortar is blended by a low speed mixer to ensure that there are no lumps in it. Waterproofing tape is placed and embeded on the fresh 1st layer mortar at corners and joints by gently pressing with a small brush.
After taping is finished, HYDRO-W10 mortar is applied as 1 mm on the surface in one direction brush strokes as 1st layer by a roller or brush. If application area is bigger than 5 m², flex THERMMESH-A1 glass-fiber mesh is placed on the mortar while 1st layer mortar surface is still fresh. Mesh is embeded on fresh mortar by gently pressing with a brush or roller. To prevent crack formation, glass-fiber mesh should be placed as endpoints min. 10 cm overlapped. To prevent crack formation at corners and joints, mesh should be applied with a 1 cm overlay on the edge of the waterproofing tape.
After 6 hours from 1st layer application (before surface completely dry), prepared HYDRO-W10 mortar is applied on the entire surface in reverse direction brush strokes with a 1 mm thickness as 2nd layer. If 1st layer surface is dry, it should be humidified before 2nd layer application. During the application, make sure that there is no space, hole or area without mortar at surface. Make sure that every mortar layer covers the application surface completely. After setting time is completed, surface becomes ready for other applications on it. At lightly loaded areas there may not need to apply a coating material on HYDRO-W10. However, in all applications, protecting the product surface from external environmental effects with a coating material application will extend the life of water isolation. If a caoting material will be applied on HYDRO-W10, minimum C2 type tile adhesive should be used for fixing. If a caoting material will not be applied on HYDRO-W10, to improve the surface strength at least 3 layers application is recommended.
Ambient and surface temperature should be between +5 ̊C and +30 ̊ during the application.
Any additional material (such as lime, cement, gypsum etc.) should not be added in to prepared mortar.
Mortar should not be applied on frozen, melting or within 24 hours danger of frost surfaces.
Hardened-set mortar should not be used by adding water and mixing again.
Mortar should not be applied on unsound and loose surfaces.
Surface should be protected from direct sunlight, extreme wind and rain during and after the application.